Method of manufacturing phase shift mask and phase shift mask

ABSTRACT

Phase shift mask which is a single side engraving type phase shift mask, which comprises a shifter part and a non-shifter part adjacent mutually on a substrate, and a shading layer pattern formed with a shading film which covers continuously from the end of the shifter part to the adjacent end of the non-shifter part including the side wall part of a dug-down part for forming said shifter part, and wherein the side wall part inclines so that the side wall part spreads toward the substrate surface.

BACKGROUND OF THE INVENTION

[0001] 1. Field of the Invention

[0002] This invention relates to a photomask and its manufacture method, particularly, relates to a substrate engraving type phase shift mask and its manufacture method.

[0003] 2. Related Arts

[0004] The progress of optical lithography technology for forming a more detailed resist pattern on a wafer is remarkably. In such field, the phase shift method in which pattern resolution can be improved by varying phases of the light that penetrate two adjacent transparent portions on a mask mutually has been adopted.

[0005] This method carries out projection exposure on a wafer with using, as a shifter for reversing phase to one of adjoining translucent parts, a mask which is formed so that the relation d=ë/2 (n−1) might be filled, wherein d is film thickness, n is refractive index, and ëis exposure wavelength (hereinafter, the mask is called “phase shift mask”.) Since the light which passed through the shifter has reverse phase (180 gaps) to the light transmitted through the other adjoining translucent part, the optical intensity is set to 0 in the pattern boundary part, the pattern can be separated, and its resolution is improved.

[0006] As mask shape which realizes the high resolution by the above-mentioned phase shifting method, there is a shifter formation type phase shift mask as shown in FIG. 6A, which has the medium (it is also called “a phase shift film” or “shifter”) 530 by which a refractive index differs from air and which is transparent, at one of the two adjacent openings (translucent parts) 521. In the case of this mask, however, it is difficult to deposit the phase shift film which has the same refractive index as a substrate with sufficient accuracy, and further there is a problem of the multiplex reflection at the phase shift film 530.

[0007] Various substrate engraving type phase shift masks (they are also called “engraving type phase shift masks.”) which dug the transparent substrate by etching, etc., as a phase shift mask which solves these problems has been known, and particularly, the substrate engraving type phase shift mask shown in FIG. 6C and FIG. 6D is in use especially now.

[0008] The engraving type phase shift mask shown in FIG. 6C is what is called “single-side engraving type phase shift mask”, which is manufactured, as shown in FIG. 6B, by dry-etching a substrate (Qz is generally used) partway, and additionally, wet etching only the dug-down part so as to obtain the predetermined phase difference (usually 180 degrees). The engraving type phase shift mask shown in FIG. 6D is what is called “double-sides engraving type phase shift mask”, which is manufactured, as shown in FIG. 6B, by dry-etching a substrate so as to obtain the predetermined phase difference (usually 180 degrees), and additionally, wet etching the whole surface of opening parts.

[0009] In the substrate engraving type phase shift mask (what was made into predetermined phase difference (usually 180 degrees) by FIG. 6B) which is manufactured by subjecting the substrate to perpendicular dry etching simply, there is a problem that the degrees of the penetration light intensity are varied by the existence of a substrate engraving in the opening, and the substrate engraving type phase shift masks shown in FIG. 6C and FIG. 6D have been developed to solve this problem.

[0010] Generally, what is called “substrate engraving type phase shift mask” is directed to the phase shift mask which has the pattern with which the shading part which shades exposure light, and translucent part were formed on the transparent substrate having the transparent refractive index n to the exposure light of wavelength ë, and wherein translucent parts adjacent mutually are formed by digging down the transparent substrate at the translucent parts so as to satisfy the condition that d1-d2 is almost equal to ë/2 (n−1), wherein d1 is for the depth of one recess at one side, d2 for the depth of another recess adjacent to the former recess.

[0011] Hereinafter, the case where one of d1 and d2 is 0 is called “single-side engraving type phase shift mask”, and the case where both d1 and d2 are 0 is called “double-sides engraving type phase shift mask”.

[0012] Further, hereinafter, the recess having the larger recess depth (it is also called “dug-down amount”.) d1 or d2 is called “shifter part”, and the other recess having smaller recess depth is called “non-shifter part”.

[0013] The Levenson type phase shift mask etc. can be mentioned as a substrate engraving type phase shift mask.

[0014] As the substrate engraving type phase shift mask, it is applicable to the phase shift mask for KrF excimer lasers whose exposure light is the wavelength of 248 nm, the phase shift mask for ArF excimer lasers whose exposure light is the wavelength of 193 nm, and the phase shift mask for F2 excimer lasers whose exposure light is the wavelength of 157 nm.

[0015] However, when the structure of the engraving type phase shift mask as shown FIG. 6C or FIG. 6D is adopted, the eaves 525 of shading film will be formed by wet etching, and it becomes easy to generate a chip and peeling of a shading film.

[0016] Particularly, the washing tolerance after wet etching spreads remarkably, it falls, and it is impossible to perform the usual washing.

[0017] Moreover, when microstructuring of the circuit pattern will progress from now along the improvement in the speed and high-densification of a semiconductor integrated circuit, peeling of the shading film will occurs during wet etching in this structure, and it can expect easily that manufacturing becomes difficult. Recently, in order to solve the problem on this structure, in the substrate engraving type phase shift mask with which the part to be etched (shifter part) and the part to be non-etched (non-shifter part) adjoin mutually, the substrate engraving type phase shift mask having the structure where the shading film is formed so that from the end of a shifter part to the adjacent end of non-shifter part is covered continuously, and the side wall 716 of dug-down part intersects almost perpendicularly in the direction of the substrate, as shown in FIG. 7, is proposed.

[0018] If it is the mask of the structure shown in FIG. 7, since there are no eaves of a shading film, neither a chip nor peeling occurs, but the mask excellent in durability can be produced.

[0019] However, in case the substrate engraving type phase shift mask of structure as shown in FIG. 7 is produced, it is necessary to form a shading film uniformly also in the step-difference parts of a substrate.

[0020] If the shading film is formed unevenly, influence will arise for the processing accuracy at the time of plate-making, or various problems, such as a fall of washing tolerance, will occur in the thin portion of a shading film.

SUMMARY OF THE INVENTION

[0021] Thus, regarding the substrate engraving type phase shift mask with which the etching part (shifter part) and the non-etching part (non-shifter part) are adjacent mutually, a phase shift mask where the shading film is formed as shown in FIG. 7 so as to cover from the end of a shifter part to the adjacent end of non-shifter part, and can form a shading film uniformly also in the step-difference parts of a substrate has been desired.

[0022] Therefore, this invention which corresponds to this needs aims to provide a phase shift mask, being of the single-side engraving type phase shift mask, with which the etching part (shifter part) and the non-etching part (non-shifter part) are adjacent mutually, and where the shading film pattern is formed with a shading film which covers continuously from the end of a shifter part to the adjacent end of non-shifter part including the side wall part of dug-down part for forming the shifter part, and can form the shading film uniformly even in the step-difference parts of a substrate, and to provide the manufacturing method thereof.

[0023] The phase shift mask according to the first invention which solves above-mentioned problems is a single side engraving type phase shift mask which comprises a shifter part and a non-shifter part adjacent mutually on a substrate, and which has a shading layer pattern formed with a shading film which covers continuously from the end of a shifter part to the adjacent end of non-shifter part including the side wall part of dug-down part for forming the shifter part (it is also called “recess”), and wherein the side wall part inclines so that the above-mentioned side wall part may spread toward the substrate surface.

[0024] The method for manufacturing phase shift mask according to the first invention is a method for manufacturing a single side engraving type phase shift mask which comprises a shifter part and a non-shifter part adjacent mutually on a substrate, and which has a shading layer pattern formed with a shading film which covers continuously from the end of a shifter part to the adjacent end of non-shifter part including the side wall part of dug-down part for forming the shifter part (recess), and wherein the side wall part inclines so that the above-mentioned side wall part may spread toward the substrate surface, which method comprises the following steps in this order; (a) a resist pattern forming step for forming resist pattern by directly opening the shifter part to the substrate, (b) a dry etching step for forming a shifter part by using the resist pattern as an etching-proof mask, and (c) a shading layer pattern formation step by photo etching after the formation of shading film on the whole surface of the substrate, wherein the resist pattern is that shows a film decreasing so that opening width may be expanded by dry etching, and wherein the dry etching process is carried out while expanding the opening width of the resist pattern to incline the side wall part of the dug-down part so as to spread toward the substrate surface.

[0025] Further, in the resist pattern formation step, the resist pattern is formed, after applying resist directly on a substrate, by exposure drawing with photograph drawing equipment, and further subjecting to the development treatment.

[0026] By such a constitution, the phase sift mask according to the first invention is enabled to provide the phase shift mask, being of the single-side engraving type phase shift mask, with which the shifter part and the non-shifter part are adjacent mutually on a substrate, and where the shading film pattern is formed with a shading film which covers continuously from the end of a shifter part to the adjacent end of non-shifter part including the side wall part of dug-down part for forming the shifter part, and can form the shading film uniformly also in the step-difference parts of a substrate.

[0027] That is, the film formation for a shading film does not become uneven as in the case of the conventional structure of FIG. 7, since the side wall part of the shifter part is inclined so that it spreads toward the substrate surface, which can form the shading film uniformly Further, the manufacture method of the phase shift mask according to the first invention, by taking the above constitution, is enabled to provide a method for manufacturing the phase shift mask, being of the single-side engraving type phase shift mask, with which the shifter part and the non-shifter part are adjacent mutually on a substrate, and where the shading film pattern is formed with a shading film which covers continuously from the end of a shifter part to the adjacent end of non-shifter part including the side wall part of dug-down part for forming the shifter part, and can form the shading film uniformly also in the step-difference parts of a substrate.

[0028] Concretely, it is attained by performing (a) a resist pattern forming step for forming resist pattern by directly opening the shifter part to the substrate, (b) a dry etching step for forming a shifter part by using the resist pattern as an etching-proof mask, and (c) a shading layer pattern formation step by photoetching after the formation of shading film on the whole surface of the substrate, in this order, wherein the resist pattern is that shows a film decreasing so that opening width may be expanded by dry etching, and wherein the dry etching process is carried out while expanding the opening width of the resist pattern to incline the side wall part of the dug-down part so as to spread toward the substrate surface.

[0029] That is, it can be made to incline the side wall part of the sifter part with spreading toward the substrate surface, since the resist is applied directly on the substrate and then a desired pattern is formed by exposing and developing in order to etch the substrate directly, where the opening of the resist pattern is gradually enlarged along with the progress of the etching of substrate.

[0030] By inclining so that the side wall part of the shifter part spreads toward the substrate surface, when a shading layer is formed on the whole surface, the shading film shall be formed uniformly.

[0031] Moreover, since the shifter part is formed by dry etching, using the above-mentioned resist pattern as an etching-proof mask after the process for forming the resist pattern by opening the shifter part directly on the substrate, the short-cut of the process and the cost reduction can be attained.

[0032] By the way, since the shading pattern made of chromium etc. was used as an etching-proof mask on the occasion of production of the conventional substrate engraving type phase shift masks of FIG. 6C and FIG. 6D, the process was complicated, and time-wastefully.

[0033] Next, the method for manufacturing the phase shift mask according to the second invention which solves the above-mentioned problems is a method for manufacturing a single-side engraving type phase shift mask which comprises a shifter part and a non-shifter part adjacent mutually on a substrate, and which has a shading layer pattern formed with a shading film which covers continuously from the end of a shifter part to the adjacent end of non-shifter part including the side wall part of dug-down part for forming the shifter part, which method comprises the following steps in this order;

[0034] (a) a metal film pattern forming step for forming metal film pattern made of metal by opening a dug-down forming region for forming a shifter part onto one side of a substrate, which substrate is transparent to the exposure light to be used and has flat faces in both sides, (b) a dry etching step for forming the dug-down part (recess) which has a depth d0 satisfying the condition that d0 is almost equal to ë/2 (n−1), wherein ëis the wavelength of exposure light to be used, and n is the refractive index of the substrate, by digging down the substrate with the dry etching force, (c) a wet etching step for etching the whole surface at the dug-down part forming side of the substrate, after removing the metal film off, and (d) a shading layer pattern formation step for forming the shading layer pattern which has openings for exposing shifter part and non-shifter part, by photoetching a shading film formed in advance, wherein the shading film is formed on the dug-down part forming side of the substrate with covering the whole surface of the side including the side wall part of dug-down part (recess) for forming the shifter part continuously.

[0035] In the above method, the wet etching process may be characterized by being that for a 10 nm-100 nm etching.

[0036] In the above method, the wet etching process may be carried out by using hydrofluoric acid.

[0037] Alternatively, in the above method, the wet etching process may be carried out by using a heated alkali.

[0038] The phase shift mask according to this invention is a single side engraving type phase shift mask which comprises a shifter part and a non-shifter part adjacent mutually on a substrate, and which has a shading layer pattern formed with a shading film which covers continuously from the end of a shifter part to the adjacent end of non-shifter part including the side wall part of dug-down part for forming the shifter part (recess), and characterized by the fact that it is manufactured by the above mentioned method for manufacturing the phase shift mask of this invention.

[0039] Regarding this invention, what is called “substrate engraving type phase shift mask” is directed to the phase shift mask which has the pattern with which the shading part which shades exposure light, and translucent parts are formed on the transparent substrate having the transparent refractive index n to the exposure light of wavelength ë, and wherein translucent parts adjacent mutually are formed by digging down the transparent substrate at the translucent parts so as to satisfy the condition that d1-d2 is almost equal to ë/2 (n−1), wherein d1 is for the depth of one recess, d2 for the depth of another recess adjacent to the former recess, and particularly, the case where one of d1 and d2 is 0 is called “single-side engraving type phase shift mask”.

[0040] Further, regarding this invention, the recess having the larger recess depth (it is also called “dug-down amount”.) d1 or d2 is called “shifter part”, and the other recess having smaller recess depth is called “non-shifter part”.

[0041] The Levenson type phase shift mask etc. can be mentioned as single-side engraving type phase shift mask according to this invention.

[0042] The single-side engraving type phase shift mask according to this invention can be used for the phase shift mask for KrF excimer lasers whose exposure light is the wavelength of 248 nm, the phase shift mask for ArF excimer lasers whose exposure light is the wavelength of 193 nm, and the phase shift mask for F2 excimer lasers whose exposure light is the wavelength of 157 nm.

[0043] By such a constitution, the method for manufacturing phase sift mask according to the invention is enabled to provide the method for manufacturing phase shift mask, the mask being of the single-side engraving type phase shift mask, with which the shifter part and the non-shifter part are adjacent mutually on a substrate, and where the shading film pattern is formed with a shading film which covers continuously from the end of a shifter part to the adjacent end of non-shifter part including the side wall part of dug-down part for forming the shifter part, and can form the shading film uniformly also in the step-difference parts of a substrate.

[0044] By carrying out the wet etching step, which follows the dry etching step and where the metal film is removed from the whole area and then the whole surface at the dug-down part forming side of the substrate is etched, to form a uniform shading layer even in the step-difference part of a substrate at the next step of forming the shading layer all over the surface of the substrate can be realized.

[0045] Thereby, as distinct from the conventional structure of FIG. 7, the phase shift mask can be manufactured without the uneven formation of the shading film.

[0046] As an applicable substrate engraving type phase shift mask, the Levenson type phase shift mask can be mentioned, and when the wet etching process is that gives an etching of 10 nm-100 nm, it is particularly effective.

[0047] When the one-side engraving type phase shift mask is a phase shift mask for KrF excimer lasers whose exposure light is the wavelength of 248 nm, the second invention is effective. When substrate engraving type phase shift mask is that for the ArF excimer lasers whose exposure light is the wavelength of 193 nm, or that for F2 excimer lasers whose exposure light is the wavelength of 157 nm, the second invention is also effective.

[0048] In the phase shift mask according to the second invention, by taking such a constitution, it is enabled to provide a phase shift mask, the mask being of the single-side engraving type phase shift mask, with which the shifter part and the non-shifter part are adjacent mutually on a substrate, and where the shading film pattern is formed with a shading film which covers continuously from the end of a shifter part to the adjacent end of non-shifter part including the side wall part of dug-down part for forming the shifter part, and can form a shading film uniformly also in the step-difference parts (they are also called “recess”) of a substrate.

[0049] As described above, we, the inventors, offer the one-side engraving type phase shift mask according to the above first and the second inventions as a phase shift mask which can form a shading film uniformly also in the step-difference part of a substrate.

[0050] General views of concrete embodiments of the shift mask according to these inventions are shown in for example, FIG. 1I or FIG. 2I.

[0051] The mask shown in FIG. 1I is one embodiment of the shift mask according to the first invention, and wherein the side wall 116 of the dug-down part inclines so that it spreads toward the substrate surface, and the mask shown in FIG. 2I is one embodiment of the shift mask according to the second invention, and wherein the top edge part 242 of the side wall of the dug-down part and the bottom edge part 243 of the side wall are formed to be round in shape, which can make the film formation of the shading film 150 (or 250) uniform.

[0052] In the production of substrate engraving type phase shift mask of structure shown as the above-mentioned FIG. 7, or FIG. 1I or FIG. 2I, after the first plate making for the formation of dug-down part forming and engraving the substrate, a shading film is formed, and then the second plate making for the shade film pattern formation is performed, whereas in the conventional substrate engraving type phase shift mask of structure shown in FIG. 6C or FIG. 6D, plate making for the shade film pattern formation is performed at first and then shade film pattern is formed, and if necessary, which is followed by the plate making for the formation of dug-down part forming and the engraving of the substrate.

[0053] Namely, in production of the substrate engraving type phase shift mask of structure shown as FIG. 7, FIG. 1I or FIG. 2I, because of performing the first plate making for the formation of dug-down part forming and the second plate making for shading film pattern formation, the process is prolonged, and therefore to enhance the efficiency of process is called for.

[0054] Thus, in the one-side engraving type phase shift mask as shown in FIG. 7, FIG. 1I and FIG. 2I, which solves the problem about the eaves of the shading film pattern of the conventional engraving type phase shift mask as shown in FIG. 6C and FIG. 6D, and wherein the shifter part and non-sifter part are adjacent mutually, to enhance the efficiency of process is called for.

[0055] Therefore, the third invention which corresponds to this needs aims to provide a method for manufacturing a phase shift mask capable of enhancing the efficiency of process, the mask being of the one-side engraving type phase shift mask, with which the shifter part and the non-shifter part are adjacent mutually on a substrate, and where the shading film pattern is formed with a shading film which covers continuously from the end of a shifter part to the adjacent end of non-shifter part including the side wall part of dug-down part for forming the shifter part, and can form the shading film uniformly also in the step-difference parts of a substrate, and to provide the manufacturing method thereof.

[0056] The method for manufacturing phase shift mask according to the third invention which solves above-mentioned problems is that for manufacturing a single side engraving type phase shift mask which comprises a shifter part and a non-shifter part adjacent mutually on a substrate, and which has a shading layer pattern formed with a shading film which has a shading property to exposure light and which covers continuously from the end of a shifter part to the adjacent end of non-shifter part including the side wall part of dug-down part for forming the shifter part (recess), and wherein as the patterning of a dug-down part forming area for giving the shifter part, a photoresist is coated on one side of the substrate directly or via a metal film, a dug-down part forming area for giving the shifter part in the formed photoresist is selectively exposed by using a photorepeater, and then the exposed photoresist is developed to obtain the resist pattern having an opening as the dug-down part forming area.

[0057] In the above method, the resist pattern forming step comprises coating a photoresist on one side of the substrate via a metal film, selectively exposing a dug-down part forming area for giving the shifter part in the formed photoresist by using a photorepeater, and then developing the exposed photoresist to obtain the resist pattern having an opening as the dug-down part forming area, wherein the metal film is that is tolerant at least to the etching gas to be used when digging the substrate down by dry etching. Thereafter, by using this resist pattern as an etching-proof mask, the metal film exposed from the opening is etched to form a metal film pattern, then the substrate part exposed from the opening of the formed metal film pattern is dry etched to form the dug-down part, the resist pattern is removed, a metal film pattern is exfoliated, and optionally, the whole part are subjected to wet etching, washing, etc., and then the shading film which has shading property to an exposure light to be used is formed on the dug-down part forming side of the substrate, and the formed shading film is processed by the photoetching method to form the shading film pattern.

[0058] Alternatively, in the above method, the resist pattern forming step comprises coating a photoresist directly on one side of the substrate, selectively exposing a dug-down part forming area for giving the shifter part in the formed photoresist by using a photorepeater, and then developing the exposed photoresist to obtain the resist pattern having an opening as the dug-down part forming area. Thereafter, by using this resist pattern as an etching-proof mask, the substrate part exposed from the opening of the mask film pattern is etched to form the dug-down part, and then the shading film which has shading property to an exposure light to be used is formed on the dug-down part forming side of the substrate, and the formed shading film is processed by the photoetching method to form the shading film pattern.

[0059] In the above method, the digging down of the substrate part is characterized by the fact that the depth d0 of the dug-down part (recess) is almost equal to ë/2 (n−1), wherein ëis the wavelength of exposure light and n is the refractive index of the substrate.

[0060] Besides, the photorepeater, in brief, is an apparatus with which the pattern of master mask is projected with a reduced scale onto a secondary mask through a lens system by using ultraviolet rays, such as i-ray (365 nm), excimer lasers, such as KrF of 248 nm wavelength as the exposure light, and wherein the pattern is exposed repeatedly at high-speed while the position of the secondary mask is moved frequently with a predetermined pitch, and it is called “photostepper” when exposing the pattern of a parent mask on a wafer.

[0061] The “shading property to exposure light” means that it is shading to the exposure light at the time of exposing on a wafer using the produced phase shift mask.

[0062] The phase shift mask according to this invention is a single side engraving type phase shift mask which comprises a shifter part and a non-shifter part adjacent mutually on a substrate, and which has a shading layer pattern formed with a shading film which has the shading property to exposure light and which covers continuously from the end of a shifter part to the adjacent end of non-shifter part including the side wall part of dug-down part for forming the shifter part (recess), and characterized by the fact that it is manufactured by the above mentioned method for manufacturing the phase shift mask of this invention.

[0063] By such a constitution, the method for manufacturing phase sift mask according to the invention is enabled to provide the method for manufacturing phase shift mask capable of enhancing the efficiency of process, the mask being of the single-side engraving type phase shift mask, with which the shifter part and the non-shifter part are adjacent mutually on a substrate, and where the shading film pattern is formed with a shading film which has a shading property to exposure light and which covers continuously from the end of a shifter part to the adjacent end of non-shifter part including the side wall part of dug-down part for forming the shifter part, and can form the shading film uniformly also in the step-difference parts of a substrate.

[0064] In detail, to adapt the photorepeater to the platemaking for the formation of dug-down part forming area has been found in this invention, from the fact that the substrate dug-down parts serve as a repetition pattern, and from a conclusion, with respect to the one-side engraving type phase shift mask with which the shifter part and the non-shifter part are adjacent mutually on a substrate and where the shading film pattern is formed with a shading film which covers continuously from the end of a shifter part to the adjacent end of non-shifter part including the side wall part of dug-down part for forming the shifter part, that the accuracy of the platemaking for the formation of dug-down part forming area can be lower than that of the (second) platemaking for the formation of the shading film pattern. Therefore, the efficiency of process can be enhanced by applying the photorepeater to the platemaking for the formation of dug-down part forming area.

[0065] As described above, when using a photorepeater, it is possible to take exposures of the pattern at an enhanced speed repeatedly, as compared with the case using electron beam drawing exposure equipment or other photodrawing exposure equipments. Thus, once master masks that have various patterns are prepared in advance, it becomes possible to take exposure for formation of dug-down part forming area to objects of various sizes speedily.

[0066] Especially when exposing the resist which is applied directly on the substrate to which a shading film is not formed, it becomes unnecessary to consider the influence by charge rise since the exposure is done by light.

[0067] Thus, it becomes possible by using a photorepeater to aim at improvement of a throughput and a cost cut.

[0068] As a substrate engraving type phase shift mask to which the manufacturing method of this invention can be applied, the Levenson type phase shift mask is mentioned. Especially when it is applied to the line and space pattern (it is also called the“L&S pattern”.) with which the shifter parts of 1.0 μm or less and the non-shifter parts of 1.0 μm or less are arranged alternately in the shape of a lattice, applied, it is particularly effective.

[0069] When the substrate engraving type phase shift mask to be applied is a phase shift mask for KrF excimer laser whose exposure light is the wavelength of 248 nm, it is effective, and it is effective also when the mask is a phase shift mask for the ArF excimer lasers whose exposure light is the wavelength of 193 nm, or the phase shift mask for F2 excimer lasers whose exposure light is the wavelength of 157 nm.

[0070] In the phase shift mask according to the invention, by taking such a constitution, it is enabled to provide a single-side engraving type phase shift mask of the reduced cost, with which the shifter part and the non-shifter part are adjacent mutually on a substrate, and where the shading film pattern is formed with the second shading film which covers continuously from the end of a shifter part to the adjacent end of non-shifter part including the side wall part of dug-downpart (recess) for forming the shifter part.

[0071] Moreover, when the phase shift mask of this invention is a phase shift mask for KrF excimer lasers whose exposure light is the wavelength of 248 nm, it is effective, and when it is the phase shift mask for ArF excimer lasers whose exposure light is the wavelength of 193 nm, it is more effective, and when it is the phase shift mask for F2 excimer lasers whose exposure light is the wavelength of 157 nm, it is particularly effective.

BRIEF DESCRIPTION OF THE DRAWINGS

[0072]FIG. 1A-FIG. 1I are sectional views each showing a process step in one embodiment of the manufacture method of the first phase shift mask according to the invention, wherein FIG. 1I shows a partial sectional view of an embodiment of the phase shift mask according to this invention;

[0073]FIG. 2A-FIG. 2I are sectional views each showing a process step in the feature part of one embodiment of the manufacture method of the second phase shift mask according to the invention, wherein FIG. 2I shows a sectional view of the feature part of one embodiment of the phase shift mask according to this invention;

[0074]FIG. 3 is an outline process flow for explaining the feature processes of two embodiments of the manufacture method of the third phase shift mask of this invention;

[0075]FIG. 4 is an outline view for explaining exposure by the photorepeater;

[0076]FIG. 5A is a chart which shows the distribution of the optical intensity at adjoining translucent parts (line parts) on the wafer, FIG. 5B is a view which shows the arrangement of the line and space pattern;

[0077]FIG. 6A-FIG. 6D are partial sectional views each showing an example of the conventional engraving type phase shift mask;

[0078]FIG. 7 is a partial sectional view showing another example of the conventional one-side engraving type phase shift mask;

[0079]FIG. 8A-FIG. 8I are charts each showing a process step of a comparative example;

[0080]FIG. 9 is a partial sectional view showing an engraving type phase shift mask in progress of the production different from the manufacture methods of the engraving type phase shift mask shown in FIGS. 1 and FIGS. 2.

BEST MODE FOR CARRYING OUT THE INVENTION

[0081] Now, this invention will be described in detail with reference to the annexed drawings. Each embodiment shown below is, however, indicated only for the purpose of giving explanation of this invention easy, and does not limit the spirit and the scope of this invention at all. This invention is limited only by Claims annexed.

[0082] 1. Phase Shift Mask Having Inclined Side Wall Part in the Dug-down part

[0083]FIG. 1A-FIG. 1I are sectional views showing the structure at each process step in one embodiment of the manufacture method of the phase shift mask according to the first invention, wherein the structure shown in FIG. 1I is an embodiment of the phase shift mask according to this invention. FIG. 5A is a chart which shows the distribution of the optical intensity at adjoining translucent parts (line parts) on the wafer when applying the constituent of the phase shift mask of this invention to the line and space pattern and projecting light thereto, and FIG. 5B is a view which shows the arrangement of the line and space pattern.

[0084] In FIG. 1A-FIG. 1I, the numeral 110 denotes a substrate (it is also called “transparent substrate”.), 115 a dug-down part, 116 a side wall part, 120 a resist, 125 an opening, 130 a dry etching gas, 150 a shading film, 155 an opening, 160 a resist, 165 an opening, 180 an sifter part (translucent part), 185 a non-shifter part (translucent part), 190 a step-difference part, respectively. In FIG. 5A-FIG. 5B, the numeral 650 denotes an translucent part (it is also called a “line part” or a “line pattern part”) of depth d1=0 in the recess, 650A the light intensity on the wafer, 660 an translucent part (it is also called a “line part” or a “line pattern part”)of depth d2 in the recess, 660A the light intensity on the wafer, 670 a translucent part (it is also called a “line part” or a “line pattern part”), 675 the pitch between adjacent lines on the mask, 675A the pitch between lines on the projected image, 685 a shading part (shading film), 690 the profile of optical intensity (on the wafer), and 695 a thresholds, respectively.

[0085] The phase shift mask according to the first invention is illustrated with reference to FIG. 1I.

[0086] The engraving type phase shift mask in this embodiment is a single side engraving type phase shift mask which comprises a shifter part 180 and a non-shifter part 185 adjacent mutually on a substrate, and which has a shading layer pattern formed with a shading film 150 which covers from the end of a shifter part 180 to the adjacent end of non-shifter part 185 including the side wall part 116 of dug-down part 115 for forming the shifter part 180 continuously, and the side wall part 116 inclines so that the above-mentioned side wall part may spread toward the surface of substrate 110.

[0087] As a magnitude of the inclination angle é of this side wall part 116 from the plumb line v that is perpendicular to the surface of substrate 110, it is desirable to be in the range of 150 to 35°, for example, although it is not particularly limited thereto.

[0088] When the inclination angle é is within the range of 15° to 35°, as compared with the case (é=0) where it does not incline at all, the homogeneity of film formation of a shading film becomes good significantly, and such inclination is not so worrisome that the boundary between the surface flat part of the substrate 110 and dug-down part 115 becomes unclear more than necessary.

[0089] The substrate 110 and the shading layer to be used are a substrate transparent to the exposure light which is used at the time-of the projection exposure to the wafer, and a film which has shading property to the exposure light is used at the time of the projection exposure to a wafer, respectively.

[0090] Usually, as the substrate 110, a quartz substrate and a synthetic quartz substrate are typical, and as the shading film 150, those of chromium-base are typical, and a chromium monolayer, or as the occasion demands, chromium layer laminated with chromium oxide, chromium nitride, and/or chromium nitride oxide, etc. are used for.

[0091] As the exposure light, although KrF excimer laser with the wavelength of 248 nm, ArF excimer laser with the wavelength of 193 nm, and F2 excimer laser with the wavelength of 157 nm, etc. are used preferably, but limited thereto.

[0092] Usually, when the wavelength ëof the exposure light is used, the depth D0 of the dug-down, part 115 for formation of shifter part 180 is set into almost ë/2 (n−1), wherein ëis the wavelength of exposure light and n is the refractive index of the substrate 110.

[0093] Concretely, although it is not limited particularly, the depth D0 is desirable to be, for example, an amount in the range of about ë/2 (n−1) value ±5%, preferably to be about ë/2 (n−1) value ±3%, more preferably to be about /2 (n−1) value ±1%, and most preferably to be just ë/2 (n−1) value. When the depth D0 is within the range of ë/2 (n−1) value ±5%, a good phase difference as the one-side engraving type phase shift mask can be obtained.

[0094] As a pattern of a phase shift mask, for example, a phase shift mask which has the line pattern (translucent part 670) of arrangement as shown in FIG. 5B, and has one section shown in FIG. 1I may be cited.

[0095] Here, ëis the wavelength of exposure light and n is the refractive index of a substrate, and the depth of one recess of the adjacent translucent parts (line pattern) 670 is set into almost ë/2 (n−1), by digging down the substrate part which is exposed from the shading film 680.

[0096] The depth d1 of recess (the depth for dug-down) of translucent part (line part) 650 is 0, and the depth d2 of recess of translucent part (line part) 660 is almost ë/2 (n−1).

[0097] Next, one embodiment of the manufacture method of the phase shift mask according to this invention is illustrated with reference to FIG. 1A-FIG. 1I.

[0098] This embodiment is the manufacture method of a phase shift mask shown by FIG. 1I. The explanation for the manufacture method of the phase shift mask of the embodiment shown in FIG. 1I is replaced with the following description.

[0099] First, onto one side of the substrate 110 which is transparent to the exposure light of the wavelength ë, and has the refractive index n (FIG. 1A), by the conventional photo lithography method, the resist film 120 which has predetermined openings which matches to the dug-down parts to be formed is formed (FIG. 1B), then by using the obtained resist film as an etching-proof mask the dry etching is carried out (FIG. 1C), in order to obtain the dug-down parts 115 (FIG. 1D).

[0100] Since the dry etching is of anisotropic, the digging (etching) will proceed only in the direction of approximately perpendicularly to the face of the substrate.

[0101] Control of the digging depth can be done precisely for example, by using phase difference measurement device (Laser Tec MPM-248) etc.

[0102] Using fluoride-base gas such as CF4 gas and CFH3 gas as gas for etching, dry etching is carried out selectively in order to obtain the predetermined depth D0 (usually equivalent to ë/2 (n−1)).

[0103] Since the wet etching method is of isotropic and whose digging (etching) will function omnidirectionally at about a same speed, this method is not used for this step.

[0104] As the resist film 120, the used is that shows a film decreasing by dry etching, and the width of the opening 125 of a resist film is expanded gradually by the film decrease effect.

[0105] By the fact that the width of the opening 125 of resist film is enlarged gradually with the time course of the dry etching, the side wall part 116 is formed with an incline that spreads toward the substrate surface.

[0106] As the resist for forming the resist film 120, for example, IP3500 (commercialized by TOKYO OHKA KOGYO CO., LTD.), THMR-M100 (commercialized by TOKYO OHKA KOGYO CO., LTD.), etc. can be utilized, and the resist film 120 is exposed by, for example, laser drawing apparatus (for example, ALTA3000 commercialized by ETEC), or a photorepeater which is described later, for example, photorepeater transfer unit (for example, NSR-365 commercialized by Nikon).

[0107] In this exposure, the charge rise problem as come up with an electronic beam exposure apparatus can be eliminated.

[0108] Subsequently, the resist film 120 is exfoliated and removed from the substrate by a predetermined exfoliation liquid, and the substrate is washed (FIG. 1E). Then, a shading film 150 is formed on the whole area of the dug-down part 115 forming side of the substrate 110 (FIG. 1F).

[0109] As the shading film 150, those of chromium-base are typical, and a chromium monolayer, or as the occasion demands, chromium layer laminated with chromium oxide, chromium nitride, and/or chromium nitride oxide, etc. are used for.

[0110] Next, by the photolithographic method, the resist layer 160 is formed with a predetermined shape on the shading film 150 (FIG. 1G).

[0111] The areas which correspond to the shifter part and the non-shifter part of the phase shift mask to be obtained are opened in the resist layer.

[0112] The resist layer 160 is not particularly limited, as far as it can serve as etching-proof resist at the time of etching the shading film 150, it can possess a proper processing ability, and a capability of giving a resolution intended.

[0113] Next, the shading film 150 exposed from the opening 165 of the resist film 160 is removed by etching (FIG. 1H) When using chromium, chromium nitride oxide, etc. as a shading film 150, this etching may be that uses ammonium cerium nitrate solution, or a dry etching using chlorine-base gas.

[0114] Then, the resist film 160 is exfoliated and removed, and the obtained substrate is subjected to washing, etc., and eventually, the purposive substrate engraving type phase shift mask is obtained (FIG. 1I).

[0115] In FIG. 1I, numerals 180 and 185 denote a shifter part (translucent part) and a non-shifter parts (translucent part), respectively.

[0116] Besides, in the case of the phase shift mask shown in FIG. 7, as shown in FIG. 9, after the construction of the shading film 750 into the predetermined shape, the substrate 710 is etched by using as the etching-proof layer the shading film 750 and resist film 720, or the shading 750 only. Therefore, the width of opening 760 in the etching-proof layer does not changed, and thus the side wall of the dug-down part (recess) is formed without incline.

[0117] In FIG. 9, numeral 730 denotes the dry etching gas.

[0118] 2. Phase Shift Mask Having Round Shaped Bottom Edges of Side Wall of the Dug-down Part

[0119] Next, an embodiment of the second invention will be described.

[0120]FIG. 2A-FIG. 2I are sectional views showing the structure at each process step in one embodiment of the manufacture method of the phase shift mask according to the second invention, wherein the structure shown in FIG. 2I is an embodiment of the phase shift mask according to this invention. As already mentioned above, FIG. 5A is a chart which shows the distribution of the optical intensity at adjoining translucent parts (line parts) on the wafer when applying the constituent of the phase shift mask of this invention to the line and space pattern and projecting light thereto, and FIG. 5B is a view which shows the arrangement of the line and space pattern.

[0121] In FIG. 2A-FIG. 2I and FIG. 8A-FIG. 8I, the numeral 210 denotes a substrate (it is also called “transparent substrate”.), 215 a dug-down part(it is also called “recess”.), 216 a side wall part, 217 and 217 a top edges, 218 and 218 a bottom edges, 220 a metal film, 220A a metal film pattern, 225 an opening, 230 a dry etching gas, 235 a resist film, 240 a shading film, 240A a shading film pattern, 245 an opening, 250 an sifter part (translucent part), 255 a non-shifter part (translucent part), respectively. As mentioned above, in FIG. 5A-FIG. 5B, the numeral 650 denotes an translucent part (it is also called a “line part” or a “line pattern part”)of depth d1=0 in the recess, 650A the light intensity on the wafer, 660 an translucent part (it is also called a “line part” or a “line pattern part”) of depth d2 in the recess, 660A the light intensity on the wafer, 670 a translucent part (it is also called a “line part” or a “line pattern part”), 675 the pitch between adjacent lines on the mask, 675A the pitch between lines on the projected image, 680 a shading part (shading film), 690 the profile of optical intensity (on the wafer), and 695 a thresholds, respectively.

[0122] An embodiment of the manufacture method of the phase shift mask according to the first invention is illustrated with reference to FIGS. 2.

[0123] This embodiment is a method for manufacturing phase shift mask for preparing the single-side engraving type phase shift mask, with which the shifter part and the non-shifter part are adjacent mutually on a substrate, and where the shading film pattern is formed with a shading film which covers continuously from the end of a shifter part to the adjacent end of non-shifter part including the side wall part of dug-down part for forming the shifter part. Further in this embodiment, manufacturing of a single-side engraving type phase shift mask which has the line pattern (translucent part 670) of arrangement as shown in FIG. 5B, and one section thereof is shown by FIG. 2I, and wherein the translucent parts 670 adjacent mutually are formed by digging down the substrate at the areas exposed from the shading film, the substrate being transparent to the exposure light of the wavelength ëand has a refractive index n, so as to satisfy the condition that d1=0 and d2 is almost equal to ë/2 (n−1), wherein d1 is for the depth of one recess, d2 for the depth of another recess, is illustrated.

[0124] First, a substrate 210 which is flat in both sides and transparent to the exposure light of the wavelength e is prepared (FIG. 2A), and a metal film 220 is formed on one side of the substrate (FIG. 2B).

[0125] Then, the metal film is photoetched to provide a metal film pattern 220A which is made of the metal film 220, and which has as openings dug-down part forming areas which is arranged for subsequent sifter part formation on one side of the substrate 210 (it is also called “photomask blank”) (FIG. 2C).

[0126] After the growth of the metal film 220 to a substrate 210 by the sputtering method, the vapor-depositing method, etc., the resist film 235 which has predetermined openings which matches to the metal patter to be desired is formed by the conventional photo lithography method, then by using the obtained resist film as an etching-proof mask the dry etching, wet etching or the like is carried out in order to obtain the metal film pattern 220A which is made of the metal film 220 and has a desired shape.

[0127] As the substrate 210 which is flat in both sides and transparent to the exposure light of the wavelength ë, typically, quartz and synthetic quartz are used like the above mentioned first invention.

[0128] When using chromium, chromium nitride oxide, etc. as the metal film 220, this etching may be carried out also by dry etching using chlorine-base gas as etchant.

[0129] The resist to be used is not particularly limited, as far as it can possess a proper processing ability, a capability of giving a resolution intended, and anti etching property.

[0130] Then, by the dry etching using the obtained resist film 235 and the metal film pattern 220A as the etching-proof mask, the substrate is dug down to provide the depth d0 of the dug-down part (recess) which is almost equal to ë/2 (n−1). (FIG. 2D, FIG. 2E).

[0131] Control of the digging depth can be done precisely for example, by using phase difference measurement device, etc., as described above.

[0132] Since the dry etching is of anisotropic, the digging (etching) in this case will proceed only in the direction of approximately perpendicularly to the face of the substrate.

[0133] Using fluoride-base gas such as CF4 gas as etchant, dry etching is carried out to the transparent substrate part exposed from the openings.

[0134] The resist to be used is not particularly limited, as far as it can possess a proper processing ability, a capability of giving a resolution intended, and anti etching property.

[0135] In addition, it is also possible to dig down the substrate by dry etching without preparing a resist film on the metal film pattern 750, as shown in FIG. 9, depending on the case.

[0136] In FIG. 9, numerals 710, 730 and 750 denotes substrate, dry etching gas, and metal film pattern, respectively.

[0137] After the dry etching, the resist film 235 is removed, and the metal film pattern 220A made of metal film 220 is exfoliated, and the substrate is washed (FIG. 2F). Then, a wet etching is carried out to the whole area of the dug-down part 215 forming side of the substrate 210 (FIG. 2G).

[0138] Since the wet etching is of isotropic and whose digging (etching) will function omnidirectionally at about a same speed.

[0139] As the etchant for the wet etching, hydrofluoric acid solution, heat alkali solution may be used.

[0140] It is desirable that the amount of etching in the wet etching is of 10 nm-100 nm.

[0141] Next, a shading film 240 is formed on the whole area of the dug-down part 215 forming side of the substrate 210 including the side walls in the dug-down parts (recesses) for forming the shifter part (FIG. 2H), and then, by the photoetching method, a shading layer pattern 240A which is made of a shading film 140 and which has openings at shifter parts and at non-shifter parts is formed (FIG. 2I).

[0142] After forming the shading film 240 onto the substrate 210 by the sputtering method, the vapor-depositing method, etc., a resist film (not shown) which has predetermined openings which matches to the shape of shading part to be obtained is formed by the conventional photolithography method as mentioned above, then by using the obtained resist film as an etching-proof mask the dry etching, wet etching or the like is carried out in order to obtain the shading film pattern 240A which is made of the shading film 240 and has a desired shape.

[0143] Then, the resist film for the formation of shading film pattern 240A is removed, and washing is carried out.

[0144] When using chromium, chromium nitride oxide as the shading film 240, this etching may be carried out also by dry etching using chlorine-base gas as etchant.

[0145] The resist to be used is not particularly limited, as far as it can possess a proper processing ability, a capability of giving a resolution intended, and anti etching property.

[0146] Thus, the one-side engraving type phase shift mask shown in FIG. 2I can be manufactured. In this embodiment, since wet etching is carried out after exfoliating the metal film pattern 220A made of the metal film 220 (FIG. 2F), the top edge part 217 and bottom edge part 218 of the side wall 216 in the dug-down part 215 shown in FIG. 2F are shaped into round, and they become as illustrated in FIG. 2G, the top edge part 217 a and bottom edge part 218 a, respectively. Thus, at the formation of the shading film 240, the film can be uniformly formed onto these areas as with that onto the flat areas (FIG. 2H).

[0147] As the result, even when the shading pattern 240A is further formed by etching the shading film 240 and then the shifter part 250 and non-shifter part 255 is formed, the possibility of generating the shading film defects at the top edge part 217 and bottom edge part 218 of the side wall 216 in the dug-down part 215 would be eliminated.

[0148] As the grade of roundness at the top edge part 217 and bottom edge part 218 of the side wall 216 in the dug-down part 215, it is desirable to have a curvature radius in the range of about 60 to 250 nm, for example, but it is not limited thereto. When a curvature radius is within the range of 60 to 250 nm, as compared with the case where it is not roundish at all, the homogeneity of film formation of a shading film becomes good significantly, and such radius is not so worrisome that the boundary between the surface flat part of the substrate 110 and dug-down part 115 becomes unclear more than necessary.

[0149] Next, one embodiment of the phase shift mask of this invention will be described.

[0150] This example was produced by the manufacture method shown in FIG. 2, which example shows the one section to FIG. 2I, and which has the line pattern (translucent part 670) of arrangement shown in FIG. 5B. By dug down the transparent substrate part of a line pattern (translucent part 670) deep, the adjacent translucent parts in which one recess depth is d1=0 and another recess depth d2 is almost equal to ë/2 (n−1) are formed.

[0151] Wherein, ëis the wavelength of exposure light and n is the refractive index of a substrate 210.

[0152] As a substrate 210, the substrate which is transparent to the exposure light using in the projection exposure to a wafer, and as a shading layer, the film which has shading property to the exposure light using in the projection exposure to a wafer is used.

[0153] Generally, as a substrate 210, a quartz substrate and a synthetic quartz substrate are typical, similar to the substrate 110 of the first invention, and as a shading film 240, also similar to the shading film 150 of the first invention, those of chromium-base are typical, and a chromium monolayer, or as the occasion demands, chromium layer laminated with chromium oxide, chromium nitride, and/or chromium nitride oxide, etc. are used for.

[0154] Excimer lasers, such as KrF, ArF, and F2, may be used, similar to the first invention, as the exposure light, but it is not limited to thereto.

[0155] As a pattern of a phase shift mask, for example, a phase shift mask which has the line pattern (translucent part 670) of arrangement as shown in FIG. 5B, and has one section shown in FIG. 2I may be cited.

[0156] Here, ëis the wavelength of exposure light and n is the refractive index of a substrate, and the depth of one recess of the adjacent translucent parts (line pattern) 670 is set into almost ë/2 (n−1), by digging down the substrate part which is exposed from the shading film 680.

[0157] The depth d1 of recess (the depth for dug-down) of translucent part (line part) 650 is 0, and the depth d2 of recess of translucent part (line part) 660 is almost ë/2 (n−1).

[0158] Although it is not limited particularly, the depth D0 is desirable to be, for example, an amount in the range of about ë/2 (n−1) value ±5%, preferably to be about ë/2 (n−1) value ±3%, more preferably to be about /2 (n−1) value ±1%, and most preferably to be just ë/2 (n−1) value. When the depth D0 is within the range of ë/2 (n−1) value ±5%, a good phase difference as the one-side engraving type phase shift mask can be obtained.

[0159] 3. Exposure by Photorepeater

[0160] An embodiment of the third invention is now illustrated with reference to the drawings.

[0161]FIG. 3 is the outline process flow for explaining the feature process of two embodiments of the manufacture method of the third phase shift mask of this invention, and FIG. 4 is an outline view for explaining exposure by the photorepeater.

[0162] In FIG. 3, the process along by a thin line arrow is what shows the first mode of the embodiment, and the process along by a thick line arrow is what showed the second mode of the embodiment. S300-S370 show a processing steps, respectively, and the sectional views in Steps S300, S310, S311, S320, S350, S351, and S360 show the section of feature part of mask to be manufactured, respectively.

[0163] In FIG. 3, numeral 310 denotes a substrate (it is also called “transparent substrate”.), 320 a metal film, 320A a metal film pattern, 321 a opening, 330 and 335 resist films (it is also called “photoresist”.), 330A and 335A resist patterns, 331 and 336 openings, respectively. In FIG. 4, numeral 10 denotes a parent mask (it is also called “master mask”.), 10 a an exposed area, 12 a secondary mask (that is the phase shift mask to be obtained.), 12 a, 12 b, 13 c, and 12 d areas to be exposed, 13 a lens system, 14 an exposure light, and 15 an X-Y stage, respectively.

[0164] First, the feature part of one embodiment of the method for manufacturing the phase shift mask of the third invention is illustrated with reference to FIG. 3.

[0165] First, the process flow of the first mode of the embodiment is explained briefly.

[0166] The first mode is that for manufacturing a single side engraving type phase shift mask which comprises a shifter part and a non-shifter part adjacent mutually on a substrate, and which has a shading layer pattern formed with a shading film which has a shading property to exposure light and which covers continuously from the end of a shifter part to the adjacent end of non-shifter part including the side wall part of dug-down part for forming the shifter part (recess), and wherein as the patterning of a dug-down part forming area for giving the shifter part, a photoresist is coated on one side of the substrate via a metal film, a dug-down part forming area for giving the shifter part in the formed photoresist is selectively exposed by using a photorepeater, and then the exposed photoresist is developed to obtain the resist pattern having an opening as the dug-down part forming area.

[0167] However, the above-mentioned metal film should be tolerant at least to the etching gas which is used at the time of digging down a substrate deep by dry etching.

[0168] First, a substrate 310 which is flat in both sides and transparent to the exposure light (wavelength ë) is prepared (S300), and a metal film 320 is formed on one side of the substrate (S310).

[0169] As the substrate 310 transparent to the exposure light of wavelength ë, quartz and synthetic quartz are used typically.

[0170] As the metal film 320, a chromium monolayer, or layer stack wherein a chromium layer is laminated with chromium oxide, chromium nitride oxide are used typically, and it can be deposited on the substrate 310 by the sputtering method, the vapor depositing method, etc.

[0171] Then, after forming the resist film 330 all over the metal film 320 (S311), resist pattern 330A is formed by selective exposing the dug-down forming area with the photorepeater (S330), developing the exposed one (S340), in order to open the dug-down forming area (S350).

[0172] Then, the metal film 320 exposed from the opening 335 of resist pattern 330A is etched in order to form shading film pattern (S351). After that, it progresses to substrate engraving processing (S370) by using resist pattern 330A and metal film pattern 320A as an etching-proof mask.

[0173] When using one of chromium-base as mentioned above is used as the metal film 320, this etching may be that uses ammonium cerium nitrate solution, or a dry etching using chlorine-base gas as etchant.

[0174] The resist film 330 is not particularly limited, as far as it can possess a proper processing ability, a capability of giving a resolution intended, and anti etching property.

[0175] This example is enabling the enhancement of process efficiency by using the photorepeater.

[0176] Next, the flow of the second mode of an embodiment is explained briefly.

[0177] Similar with the first mode, the second mode is that for manufacturing a single side engraving type phase shift mask which comprises a shifter part and a non-shifter part adjacent mutually on a substrate, and which has a shading layer pattern formed with a shading film which has a shading property to exposure light and which covers continuously from the end of a shifter part to the adjacent end of non-shifter part including the side wall part of dug-down part for forming the shifter part (recess). However, in the second mode, as the patterning of a dug-down part forming area for giving the shifter part, a photoresist is coated directly on one side of the substrate, a dug-down part forming area for giving the shifter part in the formed photoresist is selectively exposed by using a photorepeater, and then the exposed photoresist is developed to obtain the resist pattern having an opening as the dug-down part forming area.

[0178] First, a substrate 310 which is flat in both sides and transparent to the exposure light (wavelength ë) is prepared (S300) as in the case of the first mode. Then, after forming the resist film 335 all over the one side of substrate (S320), resist pattern 335A is formed by selective exposing the dug-down forming area with the photorepeater (S330), developing the exposed one (S340), in order to open the dug-down forming area (S350).

[0179] After that, it progresses to substrate engraving processing (S370) by using resist pattern 335A and as an etching-proof mask.

[0180] The resist film 335 is not particularly limited, as far as it can possess a proper processing ability, a capability of giving are solution intended, and anti etching property.

[0181] This example is also enabling the enhancement of process efficiency by using the photorepeater.

[0182] Next, the exposure by the photorepeater is briefly illustrated with reference to FIG. 4. In order to give explanation intelligible, the following description is based on an assumption that the pattern of exposure domain 10 a in the parent mask (it is also called “master mask”) 10 shall be projected and exposed to the respective secondary masks 12 (corresponding to those of steps S311, S320 in FIG. 3) with a predetermined pitch and 2×2 matrix arrangement. However, in actually, the matrix and pitch should be aligned to the phase shift mask to be manufactured.

[0183] The secondary masks 12 are fixed to the X-Y stage 15, and by the X-Y stage 15, the secondary masks 12 are moved in X and Y directions, and it is in the state stopped in the predetermined position, operations which carries out reduction projection of the whole pattern of exposure domain 10 a in the parent mask 10 through the lens system 13 on the secondary masks 12 are carried out repeatedly.

[0184] While the relative position of the lens system 13 and the parent mask 10 is fixed, the above-mentioned operations are repeated.

[0185] Thereby, reduction projections of the whole pattern of exposure domain 10 a in the parent mask 10 are carried out by the lens system 13 to the exposed domains 12 a, 12 b, 12 c, and 12 d of the secondary masks 12, respectively. As mentioned in advance, since the substrate dug-down parts serve as a repetition pattern and the resist patterning for the formation of dug-down part forming area may be at a lower accuracy, the exposure by the photorepeater can be used for that for the above resist patterning.

[0186] Thus, the enhancement of process efficiency can be attained by using the photorepeater on the exposure of this resist patterning.

[0187] Further, the exposure accuracy of the photorepeater to be used may be also low.

[0188] There is also no necessity of using excimer lasers, such as KrF (248 nm wavelength), where the illumination-optical system becomes complicated.

[0189] Next, one example which produces the phase shift mask according to the first invention shown in the above mentioned FIG. 1I is given using the manufacture method of the phase shift mask of the second mode of the embodiment, with reference to FIG. 1A-FIG. 1I.

[0190] First, as described about the first invention mentioned above, a transparent substrate 110 (FIG. 1A) which is transparent to the exposure light (wavelength ë) and has the refractive index n is prepared. Then, as the second embodiment shown in FIG. 1, resist film formation (S320), exposure by the photorepeater (S330), developing (S340), are carried out, in order to obtain the resist film which is directly formed on the substrate, and which has predetermined openings that have shapes corresponding to those of the dug-down part to be formed (FIG. 1B).

[0191] Since the dug-down part forming area has a simple repetition pattern and the exposure is carried out by the photorepeater, the time spent for exposure can be sharply shortened, as compared with the drawing time in the case of using an electronic beam exposure equipment or photograph drawing equipment.

[0192] After that, as explained with respect to the first invention, by using the resist film 120 as an etching-proof mask, dry etching is carried out (FIG. 1C) in order to form the dug-down part 115 (FIG. 1D).

[0193] As mentioned above, since the dry etching is of anisotropic, the digging (etching) in this case will proceed only in the direction of approximately perpendicularly to the face of the substrate.

[0194] Control of the digging depth can be done, for example, by using phase difference measurement device, etc., as described above.

[0195] Since the explanations about the etching gas to be used, about the depth D0, about the resist film 120, about the exposure method for resist film 120, and about subsequent process (FIGS. 1E-1I) thereafter, are almost the same with those concerned with the first invention, the explanations are omitted at this place.

[0196] Next, one example which produces the phase shift mask according to the second invention shown in the above mentioned FIG. 2I is given using the manufacture method of the phase shift mask of the first mode of the embodiment.

[0197] First, as described about the second invention mentioned above, a transparent substrate 210 (FIG. 1A) which is transparent to the exposure light of the wavelength ë is prepared. Then, as the first embodiment shown in FIG. 3, a first metal film 220 is formed on one side of the substrate 210 (FIG. 2B, corresponding to S310 of FIG. 3), resist is formed all over the metal film 220 (corresponding to S311 of FIG. 3). After that, the exposure by the photorepeater (S330), developing (S340) are carried out, in order to obtain the resist film 235 which is formed on a side of the substrate 210 via metal film 220, and which has predetermined openings that have shapes corresponding to those of the dug-down part to be formed (corresponding to S350 of FIG. 3). Further, by using the obtained resist film 235 having desired openings as the etching-proof mask, the shading film is etched so as to etch the shading film which is exposed from the opening to provide a shading film pattern which has openings for the dug-down part forming area (FIG. 2C, corresponding to S351 of FIG. 3).

[0198] Similar to above case, since the dug-downpart forming area has a simple repetition pattern and the exposure is carried out by the photorepeater, the time spent for exposure can be sharply shortened, as compared with the drawing time in the case of using an electronic beam exposure equipment or photograph drawing equipment.

[0199] Then, as explained with respect to the second invention, and thereafter as described above, by carrying out the each steps of FIG. 2C to FIG. 2I, the above mentioned shading layer pattern 240A made of the shading film 240 and which has openings at shifter parts and at non-shifter parts is formed (FIG. 2I).

[0200] Since the explanations about the raw materials, conditions, etc., to be used in this process are almost the same with those concerned with the second invention, the explanations are omitted at this place.

EXAMPLES

[0201] Although the following examples are given and this invention is explained more concretely, the examples shown below are for only the purpose which makes an understanding of this invention easy, and this invention is not limited at all by these cited examples.

Example 1

[0202] Example 1 is an example for manufacturing of Levenson type phase shift mask for KrF which has a section view as shown schematically in FIG. 1I, and has a line pattern arrangement as shown in FIG. 5B, by using the manufacturing method shown in FIG. 1.

[0203] First, onto one side of transparent substrate 110 (FIG. 1A) which is made of a synthetic quartz substrate (henceforth “Qz substrate”) with a thickness of 6.3 mm, a resist IP3500 (commercialized by TOKYO OHKA KOGYO CO., LTD.) was coated to 4650 Å. Then, it exposed with laser drawing equipment (ALTA3000 commercialized by ETEC), negatives were developed by the inorganic alkali developing solution in order to form the resist film 120 with a predetermined form. (FIG. 1B)

[0204] Next, in order to form a shifter part, dry etching using CF₄ gas was carried out (FIG. 1C), the substrate was etched to an amount for 180° phase difference (depth: 245 nm) and the dug-down part 115 was formed (FIG. 1D). Since the film decrease of the resist film 120 was also caused accompanied with the etching of the substrate 110, the opening width pattern was spread with the time course, and finally, the etching was finished in the state where the side wall 116 of a dug-down part 115 was inclined so that it was spread toward the surface (é=20°) as shown in FIG. 1D.

[0205] Subsequently, after exfoliating the resist film 120 and carrying out washing treatment (FIG. 1E), all over the dug-down part 115 forming side of the substrate 110, a chromium film and a chromium oxide film were formed at 110 nm,and several nm (about 6-8 nm), respectively, by the sputtering method in order to form a shading film 150 (FIG. 1F)

[0206] The shading film 150 was uniformly formed on the whole area, including the side wall part 116 as well as the flat surface part of a substrate 110 and the bottom part of the dug-down part 115.

[0207] Then, on the shading film 150, resist ZEP (commercialized by Nippon Zeon Co., Ltd.) was applied, it was drown with an electronic beam drawing equipment HL800 (commercialized by Hitachi, Inc.), negatives were developed by the inorganic alkali developing solution, and the resist film 160 was formed at predetermined form (FIG. 1G).

[0208] The shading film 150 which was exposed from the openings 165 of the resist film 160 and which comprised the chromium oxide and chromium was then dry etched by a mixed gas which includes chlorine as the main ingredients (FIG. 1H).

[0209] Thereafter, the resist film was exfoliated with a predetermined exfoliation liquid, washing treatment was carried out, and thereby, the one-side engraving type phase shift mask of this invention shown in FIG. 1I was produced.

[0210] This obtained the phase shift mask which is shown in FIG. 5B and where the opening size of the shading film 680 of the line pattern (translucent part) 650 in the dug-down part was made into 0.6 μm , and the opening size of the shading film 680 of the line pattern (translucent part) 660 of the not dug-down part (the recess depth is 0) was made into 0.6 μm, and the pitch of these openings was set to 1.2 μm.

[0211] The projection exposure was carried out on the wafer using the thus obtained one-side engraving type phase shift mask. After development, the resist image of the line pattern 660 (translucent part) in the mask dug-down part and the resist image of the line pattern 650 (translucent part) in the part into which a digging of a mask was not put (recess depth=0) were formed with the same size.

[0212] As a result of measuring the optical intensity on a wafer using the simulator MSM100 commercialized by the Laser Tech Company, etc., it became as shown in FIG. 5A.

[0213] The optical intensity profile 690 on a wafer became as shown in FIG. 5A, and a difference was hardly seen between the optical intensities 650A and 660A on the wafer with respect to the adjacent line patterns corresponding to the line pattern parts (translucent parts) 650 and 660, respectively.

Example 2

[0214] Example 2 is an example for manufacturing of Levenson type phase shift mask for KrF which has a section view as shown schematically in FIG. 2I, and has a line pattern arrangement as shown in FIG. 5B, by using the manufacturing method shown in FIGS. 2A-2I.

[0215] First, onto one side of transparent substrate 210 (FIG. 2A) which is made of a synthetic quartz substrate (henceforth “Qz substrate”) with a thickness of 6.3 mm, a photomask blank (FIG. 2B) which is made of the metal film 220 comprising chromium (110 nm in thickness) and chromium oxide (6-8 nm in thickness) was layered. Then, onto the metal film 220, a resist ZEP (commercialized by Nippon Zeon Co., Ltd.) was coated to 300 Å. Then, it was drawn with electronic beam drawing equipment HL800 (commercialized by Hitachi, Inc.), and negatives are developed by the inorganic alkali developing solution in order to form the resist film (not shown) with a predetermined form. Next, the metal film 220 which is formed with chromium oxide and chromium located at the opening was dry etched by a chlorine-base gas, and thereafter the resist film was exfoliated (FIG. 2C).

[0216] Next, a dry etching using CF₄ gas was carried out in order to form the shifter part, the substrate 210 was dug down so that the depth of dug-down part (recess) was almost equal to ë/2 (n−1) (depth: 245 nm), wherein ëis the wavelength of exposure light, and n is the refractive index of the substrate 210 (FIG. 2D, FIG. 2E).

[0217] The resist film 235 was removed, and the metal film 220 was exfoliated (FIG. 2F), and 40 nm wet etching was performed all over substrate 210 using hydrofluoric acid solution.

[0218] Thereby, the upper edge 217 a and the bottom edge 218 a in the substrate dug-down part 215 were round (curvature radius of about 100 nm) (FIG. 2G).

[0219] Sputtering formation of the shading film 240 which comprised chromium oxide (6-8 nm in thickness) and chromium (110 nm in thickness) was carried out all over the dug-down part 215 forming side of substrate 210 (FIG. 2H).

[0220] Since the shading film 240 was formed in the state where the upper edge 217 a and the bottom edge 218 a in the substrate dug-down part 215 were round (FIG. 1G), the films were uniformly formed on the whole area, including the area around the upper edge 217 a and the area around the bottom edge 218 a in the substrate dug-down part 215 as well as the other flat surface part of the substrate.

[0221] Then, on the shading film 240, resist ZEP (commercialized by Nippon Zeon Co., Ltd.) was applied to 3000 Å, it was drown with an electronic beam drawing equipment HL800 (commercialized by Hitachi, Inc.), negatives were developed by the inorganic alkali developing solution, and the resist film was formed at predetermined form. Further, the shading film 240 which was exposed from the openings and which comprised the chromium oxide and chromium was dry etched by a chlorine-base gas. Thereafter, the resist film was exfoliated with a predetermined exfoliation liquid, washing treatment was carried out, and thereby, the one-side engraving type phase shift mask of this invention shown in FIG. 2I was produced.

[0222] This obtained the phase shift mask which is shown in FIG. 5B and where the opening size of the shading film 680 of the line pattern (translucent part 650) in the dug-down part was made into 0.6 μm, and the opening size of the shading film 680 of the line pattern (translucent part 660) of the not dug-down part (the recess depth is 0) was made into 0.6 μm, and the pitch of these openings was set to 1.2 μm.

[0223] The projection exposure was carried out on the wafer using the thus obtained one-side engraving type phase shift mask. After development, the resist image of the line pattern (translucent part 650) in the mask dug-down part and the resist image of the line pattern (translucent part 660) in the part into which a digging of the mask was not put (recess depth=0) were formed with the same size.

[0224] As a result of measuring the optical intensity on a wafer using the simulator MSM100 commercialized by the Laser Tech Company, etc., it became as shown in FIG. 5A.

[0225] The optical intensity profile 690 on a wafer became as shown in FIG. 5A, and a difference was hardly seen between the optical intensities 650A and 660A on the wafer with respect to the adjacent line patterns corresponding to the line pattern parts (translucent parts) 650 and 660, respectively.

Comparative Example 1

[0226] This comparative example will be illustrated with reference to FIG. 8.

[0227] The process was advanced to FIG. 8C (equivalent to FIG. 2C) as is the case with Example 2.

[0228] Next, a dry etching using CF₄ gas was carried out in order to form the shifter part, the substrate 210 was dug down so that the depth of dug-down part (recess) was stopped almost equal to [ë/2 (n−1)]×(65/180), wherein ëis the wavelength of exposure light, and n is the refractive index of the substrate 210 (FIG. 8D, FIG. 8E).

[0229] From this state, further, with hydrofluoric acid solution, wet etching was carried out, so as to obtain the depth of dug-down part (recess) was almost equal to ë/2 (n−1) (FIG. 8F).

[0230] Subsequently, the above-mentioned resist film 235 was removed and the metal film 220 was exfoliated with predetermined liquid (FIG. 8G).

[0231] After carrying out washing treatment, as is the case with Example, sputtering formation of the shading film 240 which comprised chromium and chromium oxide was carried out all over the dug-down part 215 forming side of substrate 210 (FIG. 8H).

[0232] In this Comparative Example, since the top edge 217 of the dug-down part 215 of the substrate 210 was not round, the film formation of the shading film 240 was not uniformly performed at this portion.

[0233] Then, as is the case with Example, photoetching was performed. Etching of the shading film 240 was carried out in order to form the shifter part 250 and the non-shifter part 255 in predetermined shapes, and thereby, the one-side engraving type phase shift mask was manufactured.

[0234] In the case of the Comparative Example, since the top edge 217 of the dug-down part 215 of the substrate 210 was not round, film formation of the shading film 240 in this portion became uneven, and peeling occurred in washing processing.

[0235] Although it was confirmed that the shading film 240 maybe formed uniformly if wet etching was further performed all over the dug-down part 215 forming side of the substrate 210 after the state of FIG. 8G, it becomes in addition, less realistic since to perform wet etching on the whole surface with such a structure was so severe from the problem of processes, such as alignment drawing accuracy.

Example 3

[0236] Example 3 is an example for manufacturing of Levenson type phase shift mask for KrF which is as shown in FIG. 2I and has a line pattern arrangement as shown in FIG. 6B, by using the manufacturing process to which the first mode of process shown in FIG. 3 was applied and which is almost similar with the process shown in FIGS. 2.

[0237] First, onto one side of transparent substrate 210 (FIG. 2A) which is made of a synthetic quartz substrate (henceforth “Qz substrate”) with a thickness of 6.3 mm, a photomask blank (FIG. 2B) which is made of the metal film 220 comprising chromium (110 nm in thickness) and chromium oxide (several nm in thickness) was layered. Then, onto the metal film 220, a resist IP3500 (commercialized by TOKYO OHKA KOGYO CO., LTD.) was coated to 4650 Å. Then, it was subjected to a proper exposure by photorepeater transfer equipment NSR-RE365 (commercialized by NIKON) in order to open the dug-down part forming area of the resist (corresponding to S330 of FIG. 3).

[0238] Incidentally, the photorepeater transfer equipment NSR-RE365 (commercialized by NIKON) is that of using the ultraviolet ray of 365 nm wavelength as the exposure light, and that features the capability of exposing a larger pattern than the exposure area thereof by connecting and exposing two or more master masks.

[0239] Subsequently, negatives were developed by the inorganic alkali developing solution. After thus forming the resist pattern which consists of a resist film 234 which has a predetermined opening on the metal film 220, dry etching of the metal film 220 which consists of chromium oxide and chromium and which was exposed from the opening of this resist film was carried out by using a chlorine-base gas in order to form a metal film pattern 220A.

[0240] Next, a dry etching using CF₄ gas was carried out in order to form the shifter part, the substrate 210 was dug down so that the depth of dug-down part (recess) was almost equal to ë/2 (n−1) (depth: 245 nm), wherein ë is the wavelength of exposure light, and n is the refractive index of the substrate 210 (corresponding to FIG. 2D, FIG. 2E) The resist film 234 was removed, and the metal film pattern 220A was exfoliated (FIG. 2 F), and 40 nm wet etching was performed all over substrate 210 using hydrofluoric acid solution.

[0241] Thereby, the upper edge 217 a in the substrate dug-down part 215 were round (curvature radius of about 100 nm) (FIG. 2G).

[0242] Sputtering formation of the shading film 240 which comprised chromium (110 nm in thickness) and chromium oxide (several nm in thickness) and which has the shading property to the exposure light was carried out all over the dug-down part 215 forming side of substrate 210 (FIG. 2H).

[0243] Since the shading film 240 was formed in the state where the upper edge 217 a in the substrate dug-down part 215 were round (FIG. 1G), the films were uniformly formed on the whole area, including the area around the upper edge 217 a in the substrate dug-down part 215 as well as the other flat surface part of the substrate.

[0244] Then, on the shading film 240, resist ZEP (commercialized by Nippon Zeon Co., Ltd.) was applied, it was drown with an electronic beam drawing equipment HL800 (commercialized by Hitachi, Inc.), and negatives were developed by the inorganic alkali developing solution, thereby, the resist film (not shown) was formed at predetermined form. Further, the shading film 240 which was exposed from the openings and which comprised the chromium oxide and chromium was dry etched by a chlorine-base gas. Thereafter, the resist film was exfoliated with a predetermined exfoliation liquid, washing treatment was carried out, and thereby, the one-side engraving type phase shift mask of this invention shown in FIG. 2I was produced.

[0245] This obtained the phase shift mask which is shown in FIG. 5B and where the opening size of the shading film 680 of the line pattern (translucent part 650) in the dug-down part was made into 0.6 μm , and the opening size of the shading film 680 of the line pattern (translucent part 660) of the not dug-down part (the recess depth is 0) was made into 0.6 μm , and the pitch of these openings was set to 1.2 μm.

[0246] The projection exposure was carried out on the wafer using the thus obtained one-side engraving type phase shift mask. After development, the resist image of the line pattern (translucent part 650) in the mask dug-down part and the resist image of the line pattern (translucent part 660) in the part into which a digging of the mask was not put (recess depth=0) were formed with the same size.

[0247] As a result of measuring the optical intensity on a wafer using the simulator MSM100 commercialized by the Laser Tech Company, etc., it became as shown in FIG. 5A.

[0248] The optical intensity profile 690 on a wafer became as shown in FIG. 5A, and a difference was hardly seen between the optical intensities 650A and 660A on the wafer with respect to the adjacent line patterns corresponding to the line pattern parts (translucent parts) 650 and 660, respectively.

Example 4

[0249] As is the case with Example 3, Example 4 is an example for manufacturing of Levenson type phase shift mask for KrF which is as shown in FIG. 1I and has a line pattern arrangement as shown in FIG. 5B, by using the manufacturing process to which the second mode of process shown in FIG. 3 was applied and which is almost similar with the process shown in FIGS. 1.

[0250] Now, referring to FIGS. 1 and FIG. 3, this example will be illustrated.

[0251] First, onto one side of transparent substrate 210 (FIG. 1A) which is made of a synthetic quartz substrate (henceforth “Qz substrate”) with a thickness of 6.3 mm, a resist IP3500 (commercialized by TOKYO OHKA KOGYO CO., LTD.) was coated to 4650 Å. Then, as is the case with Example 3, it was subjected to a proper exposure by photorepeater transfer equipment NSR-RE365 (commercialized by NIKON) in order to open the dug-down part forming area of the resist (corresponding to S330 of FIG. 3).

[0252] Subsequently, negatives were developed by the inorganic alkali developing solution. After thus forming the resist pattern which consists of a resist film 120 which has a predetermined opening on the substrate 110, dry etching of the substrate which was exposed from the opening of this resist film was carried out by using CF₄ gas (FIG. 1C), in order to form dug-down part 115 (FIG. 1D).

[0253] The substrate 110 was dug down so that the depth of dug-down part (recess) was almost equal to ë/2 (n−1) (depth: 245 nm), wherein ëis the wavelength of exposure light, and n is the refractive index of the substrate 110.

[0254] Since the film decrease of the resist film 120 was also caused accompanied with the etching of the substrate 110, the opening width pattern was spread with the time course, and finally, the etching was finished in the state where the side wall 116 of a dug-down part 115 was inclined so that it was spread toward the surface (é=20°) as shown in FIG. 1D.

[0255] Subsequently, after exfoliating the resist film 120 and carrying out washing treatment (FIG. 1E), all over the dug-down part 115 forming side of the substrate 110, a chromium film and a chromium oxide film were formed at 110 nm,and several nm (about 6-8 nm), respectively, by the sputtering method in order to form a shading film 150 (FIG. 1F).

[0256] The shading film 150 was uniformly formed on the whole area, including the side wall part 116 as well as the flat surface part of a substrate 110 and the bottom part of the dug-down part 115.

[0257] Then, on the shading film 150, resist ZEP (commercialized by Nippon Zeon Co., Ltd.) was applied, it was drown with an electronic beam drawing equipment HL800 (commercialized by Hitachi, Inc.), negatives were developed by the inorganic alkali developing solution, and the resist film 160 was formed at predetermined form(FIG. 1G).

[0258] The shading film 150 which was exposed from the openings 165 of the resist film 160 and which comprised the chromium oxide and chromium was then dry etched by a mixed gas which includes chlorine as the main ingredients (FIG. 1H)

[0259] Thereafter, the resist film was exfoliated with a predetermined exfoliation liquid, washing treatment was carried out, and thereby, the one-side engraving type phase shift mask of this invention shown in FIG. 1I was produced.

[0260] This obtained the phase shift mask which is shown in FIG. 5B and where the opening size of the shading film 680 of the line pattern (translucent part) 650 in the dug-down part was made into 0.6 μm , and the opening size of the shading film 680 of the line pattern (translucent part) 660 of the not dug-down part (the recess depth is 0) was made into 0.6 μm , and the pitch of these openings was set to 1.2 μm.

[0261] The projection exposure was carried out on the wafer using the thus obtained one-side engraving type phase shift mask. After development, the resist image of the line pattern 660 (translucent part) in the mask dug-down part and the resist image of the line pattern 650 (translucent part) in the part into which a digging of a mask was not put (recess depth=0) were formed with the same size.

[0262] As a result of measuring the optical intensity on a wafer using the simulator MSM100 commercialized by the Laser Tech Company, etc., it became as shown in FIG. 5A.

[0263] The optical intensity profile 690 on a wafer became as shown in FIG. 5A, and a difference was hardly seen between the optical intensities 650A and 660A on the wafer with respect to the adjacent line patterns corresponding to the line pattern parts (translucent parts) 650 and 660, respectively. 

1. Phase shift mask which is a single side engraving type phase shift mask, which comprises: a shifter part and a non-shifter part adjacent mutually on a substrate, and a shading layer pattern formed with a shading film which covers continuously from the end of said shifter part to the adjacent end of said non-shifter part including the side wall part of a dug-down part for forming said shifter part, and wherein the side wall part inclines so that the side wall part spreads toward the substrate surface.
 2. Method for manufacturing phase shift mask, wherein the mask is a single side engraving type phase shift mask which comprises a shifter part and a non-shifter part adjacent mutually on a substrate, and a shading layer pattern formed with a shading film which covers continuously from the end of said shifter part to the adjacent end of said non-shifter part including the side wall part of a dug-down part for forming said shifter part, and wherein the side wall part inclines so that the side wall part spreads toward the substrate surface, which method comprises the following steps in this order; (a) a resist pattern forming step for forming resist pattern by directly opening the shifter part to the substrate, (b) a dry etching step for forming a shifter part by using the resist pattern as an etching-proof mask, and (c) a shading layer pattern formation step by photoetching after the formation of shading film on the whole surface of the substrate, wherein the resist pattern is that shows a film decreasing so that opening width may be expanded by dry etching, and wherein the dry etching process is carried out while expanding the opening width of the resist pattern to incline the side wall part of the dug-down part (recess) so as to spread toward the substrate surface.
 3. Method for manufacturing phase shift mask according to claim 2, wherein the resist pattern formation step comprises applying resist directly on a substrate, exposure drawing with photograph drawing equipment, and further subjecting exposed resist to the development treatment to form the resist pattern.
 4. Method for manufacturing phase shift mask, wherein the mask is a single-side engraving type phase shift mask which comprises a shifter part and a non-shifter part adjacent mutually on a substrate, and a shading layer pattern formed with a shading film which covers continuously from the end of said shifter part to the adjacent end of said non-shifter part including the side wall part of a dug-down part for forming said shifter part, which method comprises the following steps in this order; (a) a metal film pattern forming step for forming metal film pattern made of metal by opening a dug-down forming region for forming a shifter part onto one side of the substrate, which substrate is transparent to the exposure light to be used and has flat faces in both sides, (b) a dry etching step for forming the dug-down part (recess) which has a depth d0 satisfying the condition that d0 is almost equal to ë/2 (n−1), wherein ë is the wavelength of exposure light to be used, and n is the refractive index of the substrate, by digging down the substrate with the dry etching force, (c) a wet etching step for etching the whole surface at the dug-down part forming side of the substrate, after removing the metal film off, and (d) a shading layer pattern formation step for forming the shading layer pattern which has openings for exposing shifter part and non-shifter part, by photoetching a shading film formed in advance, wherein the shading film is formed on the dug-down part forming side of the substrate with covering continuously the whole surface of the side including the side wall part of dug-down part (recess) for forming the shifter part.
 5. Method for manufacturing phase shift mask according to claim 4, wherein the wet etching process is that gives an etching of 10 nm-100 nm.
 6. Method for manufacturing phase shift mask according to claim 4 or claim 5, wherein the wet etching process is carried out by using hydrofluoric acid.
 7. Method for manufacturing phase shift mask according to claim 4 or claim 5, wherein the wet etching process is carried out by using a heated alkali.
 8. Phase shift mask which is a single side engraving type phase shift mask, which comprises: a shifter part and a non-shifter part adjacent mutually on a substrate, and a shading layer pattern formed with a shading film which covers continuously from the end of said shifter part to the adjacent end of said non-shifter part including a side wall part of a dug-down part for forming said shifter part (recess), and characterized by the fact that it is manufactured by the method for manufacturing the phase shift mask according to one of claims 4-7.
 9. Method for manufacturing phase shift mask, wherein the mask is a single-side engraving type phase shift mask which comprises a shifter part and a non-shifter part adjacent mutually on a substrate, and a shading layer pattern formed with a shading film which has a shading property to exposure light and which covers continuously from the end of said shifter part to the adjacent end of said non-shifter part including the side wall part of a dug-down part for forming said shifter part, and wherein as the patterning of a dug-down part forming area for giving said shifter part, a photoresist is coated on one side of the substrate directly or via a metal film, a dug-down part forming area for giving said shifter part in the formed photoresist is selectively exposed by using a photorepeater, and then the exposed photoresist is developed to obtain the resist pattern having an opening as the dug-down part forming area.
 10. Method for manufacturing phase shift mask according to claim 9, wherein the resist pattern forming step comprises: coating a photoresist on one side of the substrate via a metal film, selectively exposing a dug-down part forming area for giving the shifter part in the formed photoresist by using the photorepeater, and then developing the exposed photoresist to obtain a resist pattern having an opening as the dug-down part forming area, wherein the metal film is that is tolerant at least to the etching gas to be used when digging the substrate down by dry etching, and, thereafter, while using the resist pattern as an etching-proof mask, etching the metal film at the part exposed from the opening in order to form a metal film pattern, then dry etching the substrate at the part exposed from the opening of the formed metal film pattern in order to form the dug-down part, removing the resist pattern, exfoliating the metal film pattern, optionally, wet etching the whole part, and washing, etc., and then applying the shading film which has shading property to an exposure light to be used on the dug-down part forming side of the substrate, and forming the shading film pattern made of the shading film by the photoetching method.
 11. Method for manufacturing phase shift mask according to claim 9, wherein the resist pattern forming step comprises: coating a photoresist directly on one side of the substrate, selectively exposing a dug-down part forming area for giving the shifter part in the formed photoresist by a photorepeater, and then developing the exposed photoresist in order to obtain the resist pattern having an opening as the dug-down part forming area, and thereafter, while using the resist pattern as an etching-proof mask, etching the substrate part at a part exposed from the opening of the mask in order to form the dug-down part, applying the shading film which has shading property to an exposure light to be used on the dug-down part forming side of the substrate, and forming the shading film pattern made of the shading film by the photoetching method.
 12. Method for manufacturing phase shift mask according to claims 9-11, wherein the digging down of the substrate part is characterized by the fact that the depth d0 of the dug-down part (recess) is almost equal to ë/2 (n−1), wherein ë is the wavelength of exposure light and n is the refractive index of the substrate.
 13. Phase shift mask which is a single side engraving type phase shift mask, which comprises: a shifter part and a non-shifter part adjacent mutually on a substrate, and a shading layer pattern formed with a shading film which has the shading property to exposure light and which covers continuously from the end of a shifter part to the adjacent end of non-shifter part including the side wall part of dug-down part for forming the shifter part (recess), and characterized by the fact that it is manufactured by the method for manufacturing the phase shift mask according to claims 9-12.
 14. Method for manufacturing phase shift mask according to claim 2 or claim 3, wherein the (a) step comprises: at the patterning of the dug-down part forming area for giving the shifter part, coating a photoresist directly on one side of the substrate, selectively exposing a dug-down part forming area for giving the shifter part in the formed photoresist by a photorepeater, and then developing the exposed photoresist in order to obtain the resist pattern having an opening as the dug-down part forming area.
 15. Method for manufacturing phase shift mask according to one of claims 4-7, wherein the (a) step comprises: coating a photoresist on one side of the substrate via metal film, selectively exposing a dug-down part forming area for giving the shifter part in the formed photoresist by a photorepeater, and then developing the exposed photoresist in order to obtain the resist pattern having an opening as the dug-down part forming area, while using the obtained resist pattern as an etching-proof mask, etching the metal film at a part exposed from the opening of the resist pattern in order to form the metal film pattern. 